(1)再结晶硬化后表面镜向光泽度应有较明显的提高，没有磨损的仿大理石电梯门套再结晶硬化处理后的光泽度应该超过该仿大理石电梯门套的国家标准。有磨损失光现象的仿大理石电梯门套再结晶硬化处理后应出现明显再结晶硬化层，仿大理石电梯门套表面的光泽度，至少提高10~15个光泽度单位。

(1) recrystallization after hardening surface mirror to gloss should significantly improve, no wear and tear of imitation marble elevator door recrystallization hardening treatment after gloss should exceed the national standards for the imitation marble elevator door. Wear loss of optical phenomena of imitation marble elevator door recrystallization sclerosis treatment should appear obvious recrystallization hardening layer, imitation marble elevator door surface gloss, at least raise 10 to 15 gloss units.

（2)再结晶硬化处理不可改变仿大理石电梯门套颜色，表面仿大理石电梯门套晶硬剂痕迹，无钢丝棉痕迹、磨痕和划伤等，整体干燥、干净、光泽度、清晰度统一。
(2) recrystallization hardening treatment not imitation marble elevator door color change and surface imitation marble elevator door crystal hardening agent traces, no traces of steel cotton, grinding marks and scratches, the overall dry, clean, gloss and clarity.
(3)再结晶硬化表面应具有一定的防滑性，经过再结晶硬化处理的仿大理石电梯门套表面防滑性应达到国家防滑标准。
(3) recrystallization hardening surface should have non slip, after recrystallization hardening treatment of imitation marble elevator door slip surface of should reach national standard for slip resistance.
（4)根据国家现行标准并结合我们实际操作经验仿大理石电梯门套整体研磨及再结晶硬化处理后，仿大理石电梯门套的光泽度应达到85度以上，大理石的光泽度应达到80度以上，微晶石的光泽度应达到85度以上，人造合成石的光泽度应达到75度以上，水磨石的光泽度应达到75度以上，陶瓷砖的光泽度应达到75度。
(4) according to the current national standard and combined with our practical experience imitation marble elevator door pocket integral grinding and hardening process of recrystallization after, the glossiness of the imitation marble elevator door should reach above 85 degrees, the glossiness of the marble should reach above 80 degrees, the glossiness of the microcrystalline stone should reach above 85 degrees, the glossiness of the artificial synthetic stone should reach above 75 degrees, the glossiness of the terrazzo should reach above 75 degrees, the glossiness of ceramic tile should reach 75 degrees.
本文的内容来自：仿大理石线条 详情内容请点击：http://haohui.winbrand.cc
The content of this article comes from: the imitation marble line details please click: http://haohui.winbrand.cc