1、水泥型人造石塑UV板这种人造石塑UV板是以各种水泥作为粘结剂，砂为细骨料，碎大 理石、花岗石、工业废渣等为粗骨料，经配料、搅拌、成型、加压蒸 养、磨光、抛光而制成，俗称水磨石。仿大理石uv板
1, cement type artificial stone plastic UV board this artificial stone plastic UV board is to cement as binder, sand as fine aggregate, large pieces of marble, granite, industrial waste residue as coarse aggregate, the ingredients, mixing, forming, pressing steam curing, polishing, and made, commonly known as the terrazzo.
2、聚酯型人造石塑UV板这种人造石塑UV板是以不饱和聚酯为粘结剂，与石英砂、大理 石、方解石粉等搅拌混合，浇铸成型，在固化剂作用下产生固化作 用，经脱模、烘干、抛光等工序而制成。我国多用此法生产人造石塑UV板。不饱和聚酯光泽好、颜色浅，可调成不同的鲜明颜色，这种树脂 粘度低、易于成型、固化快，可在常温下固化。

2, polyester based artificial stone plastic UV board this artificial stone plastic UV board is to unsaturated polyester as binder, and quartz sand, marble, calcite powder mixing, pouring and molding, under the effect of curing agent produced curing, demoulding, drying, polishing process and made. Our use of this method for producing artificial stone plastic UV board. The unsaturated polyester has good luster and light color, which can be adjusted into different bright colors. This kind of resin has low viscosity, easy molding, fast curing, and can be cured at room temperature.

3、复合型人造石塑UV板这种人造石塑UV板是以无机材料和有机高分子材料复合组成。 用无机材料将填料粘结成型后，再将坯体浸渍于有机单体中，使其 在一定条件下聚合。对板材而言，底层用低廉而性能稳定的无机材 料，面层用聚酯和大理石粉制作。
3, composite artificial stone plastic UV board this artificial stone plastic UV board is based on inorganic materials and organic polymer composite. When the filler is formed by the inorganic material, the body is immersed in the organic monomer, and the blank is polymerized under certain conditions. On board, the inorganic material is low and stable performance in the bottom, the top layer is made of polyester and marble powder production.
4、烧结型人造石塑UV板这种人造石塑UV板是将长石、石英、辉石“、方解石粉和赤铁矿粉 及少量高岭土等混合，用泥浆法制备坯料，用半干压法成型，在窑 炉中用 1000 C左右的高温烧结而成。
4 and sintered artificial stone plastic UV board this artificial stone plastic UV board is the mixture of quartz, feldspar and pyroxene, calcite powder and hematite and small amount of kaolin, billets prepared by slurry method, semi dry pressing molding method, in the kiln furnace with about 1000 C high temperature sintering and.